Titel: Micromechanical Characterisation of Ni/PU Hybrid Foams
VerfasserIn: Reis, Martin
König, Kristian
Diebels, Stefan
Jung, Anne
Sprache: Englisch
Titel: Materials
Bandnummer: 13
Heft: 17
Verlag/Plattform: MDPI
Erscheinungsjahr: 2020
Freie Schlagwörter: micromechanical testing
experimental mechanics
digital image correlation
open-cell foams
hyrid foams
microtensile
microbending
DDC-Sachgruppe: 500 Naturwissenschaften
Dokumenttyp: Journalartikel / Zeitschriftenartikel
Abstract: The computer-aided design of individual parts and the desire for weight reduction and material savings require further development of new hybrid materials. Ni/PU hybrid foams as a new hybrid material offer great potential for the production of components that are lightweight and yet can absorb large amounts of energy. The development of this structured material is at its beginning and mechanical characterisation on all scales is necessary. Experimental investigations on individual struts must be carried out on the micro scale to understand the structure-properties-relationship. Inspite of the challenges raising due to the complex geometry of the struts, tensile tests, three-point bending tests and micro sections are presented in this work. Due to the stiff Ni coating on the outer diameter of the struts, the resistance against bending is around five times as high as against tensile loading. The correlation between the behaviour of the struts and the macroscopic material behaviour validates the planned use of the foams as energy absorbers.
DOI der Erstveröffentlichung: 10.3390/ma13173746
Link zu diesem Datensatz: urn:nbn:de:bsz:291--ds-320859
hdl:20.500.11880/30240
http://dx.doi.org/10.22028/D291-32085
ISSN: 1996-1944
Datum des Eintrags: 17-Dez-2020
Fakultät: NT - Naturwissenschaftlich- Technische Fakultät
Fachrichtung: NT - Materialwissenschaft und Werkstofftechnik
Professur: NT - Prof. Dr. Stefan Diebels
Sammlung:SciDok - Der Wissenschaftsserver der Universität des Saarlandes

Dateien zu diesem Datensatz:
Datei Beschreibung GrößeFormat 
materials-13-03746-v2.pdf4,65 MBAdobe PDFÖffnen/Anzeigen


Diese Ressource wurde unter folgender Copyright-Bestimmung veröffentlicht: Lizenz von Creative Commons Creative Commons