Titel: | Effect of glass substrates on the formation of gold-silver colloids in nanocomposite thin films |
VerfasserIn: | Suyal, Ganesh Mennig, Martin Schmidt, Helmut K. |
Sprache: | Englisch |
Erscheinungsjahr: | 2004 |
Quelle: | Journal of sol gel science and technology. - 29. 2004, 1, S. 11-18 |
Kontrollierte Schlagwörter: | Glas Enzymsubstrat Substrat <Chemie> Substrat <Mikroelektronik> Gold-Silber-Scheidung Kolloidales Silber Gold Nanokomposit |
DDC-Sachgruppe: | 620 Ingenieurwissenschaften und Maschinenbau |
Dokumenttyp: | Journalartikel / Zeitschriftenartikel |
Abstract: | A sol-gel route to synthesize nanocomposite thin films containing phase separated metal colloids of gold (Au) and silver (Ag) was developed. Ag - Au colloids were prepared in silica films using dip coating technique. The annealing of the samples in air results in the formation of phase separated Ag and Au colloids in SiO2 thin films, showing the surface plasmon peaks at 410 nm and 528 nm. For the synthesis of phase separated Ag and Au colloids on float glass substrates, formation of the silver colloids was found strongly dependent on the surface of the float glass. On the tin rich surface formation of both gold and silver colloids took place, whereas, on the tin poor surface the formation of only gold colloids was observed. The surface dependence of the formation of silver colloids was attributed to the presence of tin as Sn2+ state on the glass surface, which oxidizes into Sn4+ during heat treatment, reducing Ag+ into silver colloids. |
Link zu diesem Datensatz: | urn:nbn:de:bsz:291-scidok-30916 hdl:20.500.11880/24822 http://dx.doi.org/10.22028/D291-24766 |
Datum des Eintrags: | 26-Feb-2011 |
Fakultät: | SE - Sonstige Einrichtungen |
Fachrichtung: | SE - INM Leibniz-Institut für Neue Materialien |
Sammlung: | INM SciDok - Der Wissenschaftsserver der Universität des Saarlandes |
Dateien zu diesem Datensatz:
Datei | Beschreibung | Größe | Format | |
---|---|---|---|---|
sm200421.pdf | 272,85 kB | Adobe PDF | Öffnen/Anzeigen |
Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt.