Titel: | Development of organic-inorganic coatings for strength-preserving of glass bottles |
VerfasserIn: | Anschütz, Dieter Gier, Andreas Mennig, Martin Schmidt, Helmut K. |
Sprache: | Englisch |
Erscheinungsjahr: | 2001 |
Quelle: | Glass science and technology. - 74. 2001, 8, S. 217-222 |
Kontrollierte Schlagwörter: | Künstliche Chemie Glasflasche Stickstoffverbindungen Stickstoff-Stickstoff-Bindung Stickstoff Silane Festigkeitslehre |
DDC-Sachgruppe: | 540 Chemie |
Dokumenttyp: | Journalartikel / Zeitschriftenartikel |
Abstract: | An amino-epoxy-silane based coating system (GAMAL) for glass surfaces was developed, which can efficiently protect bottles from the damages of a bottling plant. Testing bottles with a ramp pressure tester show an identical value of about (40 ± 4) bar for conventionally hot- and cold-end coated bottles and bottles coated with the developed organic-inorganic composite (GAMAL) system. After already 2 min of wet line-simulation testing, all species of a conventionally coated probe fall short of the critical limit of 16 bar, whereas bottles coated with GAMAL (thickness about 7 µm) show a value of (21 ± 3) bar. Coating is possible by dip and spray application on cold or hot (80°C) substrates, the coating is cured at 120°C for 5 to 10 min. Additional functions such as colour or UV protection can be added easily, without reduction of the protection potential. The low content of carbon (about 0.5 g per 11 soft drink bottle) should not disturb the recycling process of such coated bottles. |
Link zu diesem Datensatz: | urn:nbn:de:bsz:291-scidok-30115 hdl:20.500.11880/24745 http://dx.doi.org/10.22028/D291-24689 |
Datum des Eintrags: | 27-Okt-2010 |
Fakultät: | SE - Sonstige Einrichtungen |
Fachrichtung: | SE - INM Leibniz-Institut für Neue Materialien |
Sammlung: | INM SciDok - Der Wissenschaftsserver der Universität des Saarlandes |
Dateien zu diesem Datensatz:
Datei | Beschreibung | Größe | Format | |
---|---|---|---|---|
sm200103.pdf | 1,22 MB | Adobe PDF | Öffnen/Anzeigen |
Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt.