Titel: | V2O5/TiO2 catalyst xerogels : method of preparation and characterization |
VerfasserIn: | Rodella, Cristiane B. Franco, Roberto W. A. Magon, Claudio J. Donoso, Jose P. Nunes, Luis A. O. Saeki, Margarida J. Aegerter, Michel A. Florentino, Ariovaldo O. |
Sprache: | Englisch |
Erscheinungsjahr: | 2002 |
Quelle: | Journal of sol-gel science and technology. - 25. 2002, S. 75-82 |
Kontrollierte Schlagwörter: | Sol-Gel-Verfahren Vanadium Vanadiumdioxid Titan Katalyse Ethanol Katalytische Oxidation Röntgendiffraktometrie |
DDC-Sachgruppe: | 620 Ingenieurwissenschaften und Maschinenbau |
Dokumenttyp: | Journalartikel / Zeitschriftenartikel |
Abstract: | This work describes a modified sol-gel method for the preparation of V2O5/TiO2 catalysts. The samples have been characterized by N2 adsorption at 77 K, X-ray diffractometry (XRD), Scanning Electronic Microscopy (SEM/EDX) and Fourier Transform Infrared Spectroscopy (FT-IR). The surface area increases with the vanadia loading from 24 m2 g-1 for pure TiO2 to 87 m2 g-1 for 9wt% of V2O5. The rutile form is predominant for pure TiO2 but becomes enriched with anatase phase when vanadia loading is increased. No crystalline V2O5 phase was observed in the diffractograms of the catalysts. Analysis by SEM showed heterogeneous granulation of particles with high vanadium dispersion. Two species of surface vanadium were observed by FT-IR spectroscopy: a monomeric vanadyl and polymeric vanadates. The vanadyl/vanadate ration remains practically constant. Ethanol oxidation was used as a catalytic test in a temperature range from 350 to 560 K. The catalytic activity starts around 380K. For the sample with 9 wt% of vanadia, the conversion of ethanol into acetaldehyde as the main product was approximately 90% at 473 K. |
Link zu diesem Datensatz: | urn:nbn:de:bsz:291-scidok-25168 hdl:20.500.11880/24326 http://dx.doi.org/10.22028/D291-24270 |
Datum des Eintrags: | 15-Dez-2009 |
Fakultät: | SE - Sonstige Einrichtungen |
Fachrichtung: | SE - INM Leibniz-Institut für Neue Materialien |
Sammlung: | INM SciDok - Der Wissenschaftsserver der Universität des Saarlandes |
Dateien zu diesem Datensatz:
Datei | Beschreibung | Größe | Format | |
---|---|---|---|---|
aeg200203.pdf | 815,93 kB | Adobe PDF | Öffnen/Anzeigen |
Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt.