Titel: | Influence of the layer morphology on the electrical properties of sol-gel transparent conducting oxide coatings |
VerfasserIn: | Goebbert, Christian Gasparro, Guido Schuler, Thomas Krajewski, Thomas Aegerter, Michel A. |
Sprache: | Englisch |
Erscheinungsjahr: | 2000 |
Quelle: | Journal of sol-gel science and technology. - 19. 2000, S. 435-439 |
Kontrollierte Schlagwörter: | Morphologie Elektrische Eigenschaft Sol-Gel-Verfahren Antimon Aluminium Tauchbeschichten Durchstrahlungselektronenmikroskopie |
DDC-Sachgruppe: | 620 Ingenieurwissenschaften und Maschinenbau |
Dokumenttyp: | Journalartikel / Zeitschriftenartikel |
Abstract: | Tranparent conducting coatings have been prepared by sol gel methods either by a conventional sol-gel process (Antimony doped Tin Oxide - ATO, Aluminium doped Zinc Oxide - AZO) or a new wet chemical process using fully dispersed crystalline nanoparticles (ATO, Indium Tin Oxide - ITO). The dip coating technique has been used as deposition technique with single coating thickness varying from a few nanometer to ca. 400 nm. The layers have been fired in a furnace. Structural properties have been determined by x-ray diffraction and TEM analysis and the electrical properties by the van der Pauw/Hall measurement. Three different coating procedures have been used to investigate the effect on the structure, morphology and the electrical properties of the coatings. It is shown that the individual layer thickness in multilayer coatings influences dramatically the mentioned properties. Very thin individual layers favour a heterogeneous nucleation with dense columnar growth of the crystallites leading to low electrical resistivity (Ω ≈ 10 -³ Ω cm), while thick individual layers result in a porous morphology made of small crystallites leading to resistivities in the 10≈2 Ω cm range. |
Link zu diesem Datensatz: | urn:nbn:de:bsz:291-scidok-25057 hdl:20.500.11880/24316 http://dx.doi.org/10.22028/D291-24260 |
Datum des Eintrags: | 14-Dez-2009 |
Fakultät: | SE - Sonstige Einrichtungen |
Fachrichtung: | SE - INM Leibniz-Institut für Neue Materialien |
Sammlung: | INM SciDok - Der Wissenschaftsserver der Universität des Saarlandes |
Dateien zu diesem Datensatz:
Datei | Beschreibung | Größe | Format | |
---|---|---|---|---|
aeg200005.pdf | 323,91 kB | Adobe PDF | Öffnen/Anzeigen |
Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt.