Titel: | Investigation of new ion-conducting ORMOLYTES : structure and properties |
VerfasserIn: | Dahmouche, Karim Atik, Mohamed Mello, Nilson C. Bonagamba, Tito J. Panepucci, Horacio Aegerter, Michel A. Judeinstein, Patrick |
Sprache: | Englisch |
Erscheinungsjahr: | 1997 |
Quelle: | Journal of sol-gel science and technology. - 8. 1997, S. 711-715 |
Kontrollierte Schlagwörter: | Lithiumion Sol-Gel-Verfahren Ionenleitung Raumtemperatur Tetraethylsilicat <Tetraethylorthosilicat> Polyethylenglykole Polymere |
DDC-Sachgruppe: | 620 Ingenieurwissenschaften und Maschinenbau |
Dokumenttyp: | Journalartikel / Zeitschriftenartikel |
Abstract: | Two families of hybrid organic-inorganic composites exhibiting Li+ ionic conduction (ORMOLYTES) have been prepared by the sol-gel process. The first family, prepared from a mixture of 3-isocyanatopropyltriethoxysilane, O,O''Bis (2-aminopropyl)-polyethyleneglycol (or O,O'Bis (2-aminopropyl)-polypropyleneglycol) and lithium salt, presents chemical bonds between the organic and the inorganic phase and an ionic conductivity σ higher than 10-4 S m-1 at room temperature. Their properties have been related to their structure using liquid state NMR measurements of 7Li between -100°C and +100'°C and the DMTA technique. In the second family, prepared by ultrasonic method from a mixture of tetraethoxysilane (TEOS), polyethyleneglycol (PEG) and lithium salt, the organic and inorganic phases are not chemically bonded. Ionic conductivity σ has been studied as a function of the polymer chain length and concentration. Values of σ up to 10-2S m-1 at room temperature have been obtained (with a silica-PEG300 system, PEG/TEOS=40% in weight). Again, structure was investigated by liquid state 7Li NMR measurements. |
Link zu diesem Datensatz: | urn:nbn:de:bsz:291-scidok-24914 hdl:20.500.11880/24306 http://dx.doi.org/10.22028/D291-24250 |
Datum des Eintrags: | 4-Dez-2009 |
Fakultät: | SE - Sonstige Einrichtungen |
Fachrichtung: | SE - INM Leibniz-Institut für Neue Materialien |
Sammlung: | INM SciDok - Der Wissenschaftsserver der Universität des Saarlandes |
Dateien zu diesem Datensatz:
Datei | Beschreibung | Größe | Format | |
---|---|---|---|---|
aeg199714.pdf | 520,18 kB | Adobe PDF | Öffnen/Anzeigen |
Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt.