Titel: | Raman and infrared investigations of glass and glass-ceramics with composition 2Na2O·1CaO·3SiO2 |
VerfasserIn: | Ziemath, Ervino C. Aegerter, Michel A. |
Sprache: | Englisch |
Erscheinungsjahr: | 1994 |
Quelle: | Journal of materials research. - 9. 1994, 1, S. 216-225 |
Kontrollierte Schlagwörter: | Präkursor Ausgangsmaterial Biologisches Material Raman-Spektrum |
DDC-Sachgruppe: | 500 Naturwissenschaften |
Dokumenttyp: | Journalartikel / Zeitschriftenartikel |
Abstract: | Precursor glass and glass-ceramics with molar composition 2Na2O·1CaO·3SiO2 are studied by infrared, conventional, and microprobe Raman techniques. The Gaussian deconvoluted Raman spectrum of the glass presents bands at 625 and 660 cm-1, attributed to bending vibrations of Si-O-Si bonds, and at 860, 920, 975 and 1030 cm-1, attributed to symmetric stretching vibrations of SiO4 tetrahedra with 4, 3, 2, and 1 nonbridging oxygens, respectively. The Raman microprobe spectrum of a highly crystallized sample presents two narrow and intense bands at about 590 and 980 cm-1, associated with vibrations of SiO4 tetrahedra with two nonbridging oxygens, in agreement with the predicted chain-like structure of crystalline metasilicates. Scanning electron microscopy shows that the crystals distributed in partially crystallized samples have a spherical shape, built up by radially oriented needle-like single crystals. The Raman microprobe spectra of these spherulites show that they still contain residual amorphous material. A comparison of Raman and infrared spectra of amorphous and highly crystallized samples is presented. |
Link zu diesem Datensatz: | urn:nbn:de:bsz:291-scidok-23513 hdl:20.500.11880/24225 http://dx.doi.org/10.22028/D291-24169 |
Datum des Eintrags: | 4-Sep-2009 |
Fakultät: | SE - Sonstige Einrichtungen |
Fachrichtung: | SE - INM Leibniz-Institut für Neue Materialien |
Sammlung: | INM SciDok - Der Wissenschaftsserver der Universität des Saarlandes |
Dateien zu diesem Datensatz:
Datei | Beschreibung | Größe | Format | |
---|---|---|---|---|
AEG224.pdf | 3,58 MB | Adobe PDF | Öffnen/Anzeigen |
Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt.