Titel: Electromigration failure by shape change of voids in bamboo lines
VerfasserIn: Arzt, Eduard
Kraft, Oliver
Nix, William D.
Sanchez, J. E.
Sprache: Englisch
Erscheinungsjahr: 1994
Quelle: Journal of applied physics. - 76. 1994, 3, S. 1563-1571
Kontrollierte Schlagwörter: Elektromigration
DDC-Sachgruppe: 620 Ingenieurwissenschaften und Maschinenbau
Dokumenttyp: Journalartikel / Zeitschriftenartikel
Abstract: The behavior of electromigration-induced voids in narrow, unpassivated aluminum interconnects is examined, using scanning electron microscopy. Some electromigration tests were interrupted several times in order to observe void nucleation, void growth, and finally the failure of the conductor line. It is found that voids which opened the line have a specific asymmetric shape with respect to the electron flow direction. Besides void nucleation and void growth, void shape changes can consume a major part of the lifetime of the conductor line. A first attempt to model these processes on the basis of diffusion along the void surface shows that voids with a noncircular initial shape tend to produce the fatal asymmetry due to electron wind effects, with the anisotropy of surface energy possibly playing only a minor role.
Link zu diesem Datensatz: urn:nbn:de:bsz:291-scidok-17468
hdl:20.500.11880/23861
http://dx.doi.org/10.22028/D291-23805
Datum des Eintrags: 12-Nov-2008
Fakultät: SE - Sonstige Einrichtungen
Fachrichtung: SE - INM Leibniz-Institut für Neue Materialien
Sammlung:INM
SciDok - Der Wissenschaftsserver der Universität des Saarlandes

Dateien zu diesem Datensatz:
Datei Beschreibung GrößeFormat 
ea199401.pdf1,36 MBAdobe PDFÖffnen/Anzeigen


Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt.